  钢构件镀锌层附着性能测定仪是检测仪器,适用于公路用钢构件镀锌层附着性能测检验使用。使用前务必仔细阅读说明书。并由**实验人员操作,以避免操作不当引起的伤害。如需了解更多资料请与我公司客服人员联系。


  The tester for galvanized layer adhesion of steel members is a testing instrument,which is suitable for testing and inspection of galvanized layer adhesion of steel members for highways.Be sure to read the instructions carefully before use.It is operated by**experimental personnel to avoid injury caused by improper operation.For more information,please contact our customer service staff.


  钢构件镀锌层附着性能测定仪适用于热浸镀锌层附着力试验,是利用锤头自由跌落击打试样来测试镀锌层附着性能质量进行评价,产品符合JT/T684-2007《钢构件镀锌层附着性能测定仪》、JT/T281-2007《高速公路波形梁钢护栏》、JT/T374-1998《隔离栅技术条件》附录中的技术指标,及GB/T2694-2010《输电线路铁塔制造技术条件》的落锤试验方法。


  The tester for the galvanized layer adhesion of steel members is suitable for the hot-dip galvanized layer adhesion test.It uses the hammer head to freely drop and hit the sample to evaluate the quality of galvanized layer adhesion.The product meets JT/T684-2007"Steel The technical indicators in the appendix of the component galvanized layer adhesion performance tester,JT/T281-2007"Highway Corrugated Beam Steel Guardrail",JT/T374-1998"Isolation Bar Technical Specifications",and GB/T2694-2010"Transmission Line"Technical conditions for manufacturing towers"drop hammer test method.


  钢构件镀锌层附着性能测定仪技术参数:


  ★锤头采用45号钢,质量为(210±10)g,表面镀铬。


  ★锤刃硬度(肖氏)不低于40HS。


  ★锤柄采用橡木,质量为(70±10)g。


  ★锤头中间线至底座面垂直高度:300mm±1mm


  ★底座采用Q235钢,尺寸为:250mm*250mm*15mm


  ★重量偏差:±1g,几何尺寸偏差:±1mm。


  ★锤头、锤柄及底座公称尺寸及允许偏差


  ★构件名称公称尺寸及允许偏差


  ★锤头L(mm)F(mm)c1(mm)a(°)锤刃切面平整度(UM)刃口宽度(mm)


  100±2 60±1 20±1 90±1≤8≤0.1


  ★锤柄A(mm)B(mm)C(mm)D(mm)Φ2 N(mm)


  275±5 100±2 105±2 27±1 20±1 15°-1


  ★底座E(mm)H(mm)G(mm)K(mm)M(mm)


  25±1 30±1 15°±1 22±1 60±1


  Technical parameters of galvanized coating adhesion tester for steel members:


  ★The hammer head is made of 45#steel with a mass of(210±10)g and its surface is chrome-plated.


  ★Hammer blade hardness(Shore)is not lower than 40HS.


  ★The hammer handle is made of oak with a mass of(70±10)g.


  ★Vertical height from center line of hammer head to base surface:300mm±1mm


  ★The base is made of Q235 steel,the size is:250mm*250mm*15mm


  ★Weight deviation:±1g,geometric dimension deviation:±1mm.


  ★Nominal size and allowable deviation of hammer head,hammer handle and base


  ★Name of component Nominal size and allowable deviation


  Hammer head L(mm)F(mm)c1(mm)a(°)Flatness of hammer cutting surface(UM)Edge width(mm)


  100±2 60±1 20±1 90±1≤8≤0.1


  Hammer shank A(mm)B(mm)C(mm)D(mm)Φ2 N(mm)


  275±5 100±2 105±2 27±1 20±1 15°-1


  Base E(mm)H(mm)G(mm)K(mm)M(mm)


  25±1 30±1 15°±1 22±1 60±1


  钢构件镀锌层附着性能测定仪材料和质量:


  ★锤头采用45号钢,质量为(210±10)g,表面镀铬。


  ★锤刃硬度(肖氏)不低于40HS。


  ★锤柄采用橡木,质量为(70±10)g。


  ★底座采用Q235钢,表面镀铬。


  Material and quality of galvanized coating adhesion tester for steel members:


  ★The hammer head is made of 45#steel with a mass of(210±10)g and its surface is chrome-plated.


  ★Hammer blade hardness(Shore)is not lower than 40HS.


  ★The hammer handle is made of oak with a mass of(70±10)g.


  ★The base is made of Q235 steel and the surface is chrome-plated.